RSF 816 G

 

  • Tg ~75°C
  • "Green" system
  • transparent
  • good UV stability
  • provides a glossy surface. (e.g. for surfboards)

 

Application fields:
For manufacturing of sport & leisure and marine composites parts

 

Biresin® CR82

 

  • Tg ~90°C
  • fast hardener for demoulding after room temperature curing
  • uniform mixing ratio
  • with GL approval

 

Application fields:
Part production and mould making applications in boat building, automotive industry and wind industry

Biresin® CR84

 

  • Tg ~100°C
  • thixotropic A-Component provides an optimal mixed viscosity
  • good wetting behaviour and good non draining properties
  • curing cycles of 12 minutes at 80°C are possible

 

Application fields:
High volume production of sport and leisure goods such as skis, snowboards, skateboards, wakeboards, surfboards etc., especially those which include a variety of materials such as glass fibre, wood, metal, plastic etc.

Biresin® CR122

 

  • Tg ~120°C
  • enables demoulding at room temperature
  • meets the standards of the European EASA construction rules (Part 22)
  • approved by Luftfahrt Bundesamt according RHV
  • with GL approval

 

Application fields:
Part production and mould making applications in light aviations, boat building, automotive and wind industry

Biresin® CR132

 

  • Tg ~140°C
  • product family with standard hardeners for a wide range of processing times
  • The same hardeners can be used for Biresin CR132 FR and CR134 FR to use it as a flame retardant wet lay-up system or with Biresin CR131 to use it for infusion or injection processes

 

Application fields:
Part production and mould making applications in boat building, aircraft industry, automotive and wind industry

Biresin® CR172

 

  • Tg ~175°C
  • nontoxic high Tg system for wet lay-up
  • good impregnation and non-draining properties
  • can be used in hand lay-up and injection process

 

Application fields:
Part production and mould making applications in boat building, automotive and wind industry, especially suitable for moulds and parts with a high heat distortion resistance

EPOLAM 2080

 

  • Tg ~190°C
  • high Tg system for wet lay-up
  • low shrinkage after curing

 

Application fields:
Suitable for moulds in aviation market, part production and mould making applications in boat building, automotive and wind industry

Biresin® CR132 FR

 

  • Tg ~130°C
  • flame retardant version of Biresin CR132
  • UL94 V-0 classification (with CH132-2) for the production of structural parts in wet lay-up

 

Application fields:
Part production with flame retardant requirements

Biresin® CR134 FR

 

  • Tg ~130°C
  • UL94 V-0 classification (with CH132-5) for the production of structural parts in wet lay-up and special processes

 

Application fields:
Part production with flame retardant requirements

EPOLAM 2500

 

  • Tg ~95°C
  • Flame retardant system for wet lay-up according FAR25.853

 

Application fields:
For use in the construction, assembly and maintenance of interior composite components on new and existing commercial aircraft