PX 221

 

  • very short demoulding time
  • flexural modulus 2,100 MPa
  • Tg ~95°C
  • high reproduction accuracy
  • can be easily pigmented with colouring CP
  • high impact resistance


Application field:

Prototype parts and mock-ups with mechanical properties similar to thermoplastics such as HIPS

PX 225 OP

 

  • flexural modulus 2,500 MPa
  • Tg ~100°C
  • good impact and flexural resistance
  • very easy colouring with all kind of pigments (not water based)


Application field:
Thermoplastic-like parts with a flexural modulus of elasticity close to 2,500 MPa (ex: polycarbonate, ABS)

PX 226

 

  • flexural modulus 2,500 MPa
  • Tg ~105°C
  • good impact and flexural resistance
  • available in 2 reactivities
  • excellent ratio pot life/demoulding time
  • high thermal resistance
  • can be easily pigmented with CP pigments


Application fields:

Prototype parts and mock-ups with mechanical properties similar to thermoplasitcs like filled ABS (e.g. household appliances; electrical components production)

Biresin® VG280

 

  • flexural modulus 2,800 MPa
  • very stiff
  • high flexural strength
  • high impact resistance
  • simulates ABS, PVC


Application fields:
Very stiff housings with high strength and impact resistance; fast and cost-effective production of high-quality prototypes and short run parts for the automotive industry and consumer goods

PX 245

 

  • flexural modulus 4,500 MPa
  • Tg ~95°C
  • high reproduction accuracy
  • available in 2 reactivities
  • can be easily coloured with CP pigments
  • fast demoulding


Application fields:

Production of highly rigid parts e.g. electronic devices casing; prototype parts with mechanical properties similar to thermoplastics like polyoxymethylene and polyamide