PX 223 HT

 
  • for the production of prototype parts and mock-ups with properties close to those of thermoplastics
  • 80 Shore D
  • flexural modulus:  334,000 psi
  • Tg 248°F

 

Applications:

system for parts out of HIPS with superior heat and impact resistance

 

 

SikaBiresin® PX 224

 

  • 83 Shore D casting urethane, parts can be post cured to reach a higher Tg temperature
  • pot life (150g mass):  6 - 9 minutes
  • Flexural Modulus, 1,829 MPa
  • Tg, 174°C-Cure #1, 200°C-Cure #2
  • Extremely tough and impact resistant
  • Hardness 83 Shore D
  • Pigmentable
     
    Applications:
    designed to give the feel of thermo plastic parts for prototype applications

 

 

TCC-8020A / TCC-8021B

 

  • 75 Shore D casting urethaneparts can be post cured to reach a higher heat deflection temperature
  • pot life (150g mass):  16 - 18 minutes
     
    Applications:
    designed to give the feel of thermo plastic parts for prototype applications

 

 

PX 221 (EUROPEAN SOURCED)

 

= XP 3771/1 (PX 221)

The documentation for PX 221 is still under the name XP 3771/1. As soon as the new documentation under the name PX 221 has been produced we will make it available.

 

  • flexural modulus 2,100 MPa
  • Tg ~95°C
  • high reproduction accuracy
  • can be easily pigmented with colouring CP
  • high impact resistance


Application field:

Prototype parts and mock-ups with mechanical properties similar to thermoplastics such as HiPS

PX 225 OP (EUROPEAN SOURCED)

 

  • flexural modulus 2,500 MPa
  • Tg ~100°C
  • good impact and flexural resistance
  • very easy colouring with all kind of pigments (not water based)


Application field:
Thermoplastic-like parts with a flexural modulus of elasticity close to 2,500 MPa (ex: polycarbonate, ABS)

PX 226 (EUROPEAN SOURCED)

 

  • flexural modulus 2,500 MPa
  • Tg ~105°C
  • good impact and flexural resistance
  • available in 2 reactivities
  • excellent ratio pot life/demoulding time
  • high thermal resistance
  • can be easily pigmented with CP pigments


Application fields:

Prototype parts and mock-ups with mechanical properties similar to thermoplasitcs like filled ABS (e.g. household appliances; electrical components production)

Biresin® VG280 (EUROPEAN SOURCED)

 

  • flexural modulus 2,800 MPa
  • very stiff
  • high flexural strength
  • high impact resistance
  • simulates ABS, PVC


Application fields:
Very stiff housings with high strength and impact resistance; fast and cost-effective production of high-quality prototypes and short run parts for the automotive industry and consumer goods

PX 245 (EUROPEAN SOURCED)

 

  • flexural modulus 4,500 MPa
  • Tg ~95°C
  • high reproduction accuracy
  • available in 2 reactivities
  • can be easily coloured with CP pigments
  • fast demoulding


Application fields:

Production of highly rigid parts e.g. electronic devices casing; prototype parts with mechanical properties similar to thermoplastics like polyoxymethylene and polyamide